I do not know of course, but I would suspect all that would happen from now on out is that you would deepen the pitting, based upon how it looks now. Put it in boiling water for a few minutes to heat up the steel and then use cold blue on it and see what happens. This would not be destructive in any way and if you don't like it you can still bleach it again.