If I've got this right, SR77 is STRONGER than SR101 and SR101 is TOUGHER than SR77. So SR77 will accept more gradually applied weight before it breaks than SR101 will but SR101 can bounce bigger, faster-moving bullets off it than SR77 can.
Do we agree with this statement?
ohhhhhhhhhh now i see the picture in your head. annealed, i don't think there will be a difference in toughness or strength between the steels. hardened to 59hrc, i can see your picture working. after that, i think we go back to either steel failing under the same conditions.